http://cimav.repositorioinstitucional.mx/jspui/handle/1004/2428| AEMM490517HDFCJR02 UV Electroluminescence from ITO/SRO/p-Si and ITO/SRN/SRO/p-Si Structures | |
| Alfredo Morales Sánchez LILIANA PALACIOS HUERTA | |
| Acceso Abierto | |
| Atribución-NoComercial | |
| Abstract—This work presents the electrical and electroluminescent properties of light emitting capacitors (LECs) using silicon rich oxide (SRO) and the effect of a thin silicon rich nitride (SRN) film on it (SRN/SRO) as active layers. LECs were fabricated using simple Metal–Insulator–Semiconductor (MIS) structures with indium tin oxide (ITO) and aluminum as gate and substrate electrodes, respectively. All devices exhibit a resistance switching (RS) behavior from a high conduction state (HCS) to a low conduction state (LCS), enhancing an intense ultraviolet-blue (UV-B) EL. This RS behavior produces structural changes in the active layer and probably in the ITO contact. Seven narrow bands with half-peak width of 7±0.6 nm at ~250, 270, 285, 305, 325, 415 and 450 nm are clearly observed once the low conduction state is reached. The red-near infrared EL at HCS is similar to the PL spectra indicating the same radiative process is involved. An increment of the EL band at ~590 nm in SRN/SRO is observed at both conduction states. This band has been observed before and attributed transitions from the minimum band conduction to K0 centers in SRN films. The UV-B emission appears at lower electric field when the SRN/SRO film is used as active layer. | |
| 2016 | |
| Artículo | |
| Inglés | |
| QUÍMICA | |
| Versión publicada | |
| publishedVersion - Versión publicada | |
| Aparece en las colecciones: | Artículos |
Cargar archivos:
| Fichero | Tamaño | Formato | |
|---|---|---|---|
| UV Electroluminescence from ITOSROp-Si and.pdf | 293.71 kB | Adobe PDF | Visualizar/Abrir |