Por favor, use este identificador para citar o enlazar este ítem:
http://cimav.repositorioinstitucional.mx/jspui/handle/1004/1535| STRESS CORROSION CRACKING ASSESSMENT OF API STEEL IN ETHANOL-GASOLINE BLENDS | |
| GABRIELA KARINA PEDRAZA BASULTO JAMNIE YAZMIN ACHEM CALAHORRA JOSE ANGEL CABRAL MIRAMONTES JOSE GUADALUPE CHACON NAVA | |
| Acceso Abierto | |
| Sin Derechos Reservados | |
| Stress corrosion cracking Ethanol | |
| The effect of water content (0.5%, 5%, and 10%V) in E85 blend and 0.5%V E10 blend on the stress corrosion cracking (SCC) susceptibility of X-52 carbon steel was investigated. Slow strain rate tests (SSRT) coupled with electrochemical noise measurements (EN) were carried out using a strain rate of 1 X 10-6s-1. In general, scanning electron microscopy (SEM) observations on fracture surfaces showed a ductile behavior. However, secondary cracking was only observed for specimens exposed to solution containing up to 5%V water. En show of a likely localized corrosion process occurring at low water concentrations, whereas for water content above 5%V, a uniform corrosion process seems more likely to occur. | |
| 2013 | |
| Memoria de congreso | |
| Inglés | |
| OTRAS | |
| Versión revisada | |
| submittedVersion - Versión revisada | |
| Aparece en las colecciones: | Artículos de Congresos |
Cargar archivos:
| Fichero | Tamaño | Formato | |
|---|---|---|---|
| 45 STRESS CORROSION CRACKING ASSESSMENT OF API STEEL IN ETHANOL-GASOLINE BLENDS.pdf | 2.78 MB | Adobe PDF | Visualizar/Abrir |